PA6 7335F|美国杜邦 PA6 7335F物性黄卡|PA6 7335F价格

发布时间:2020-09-14 18:58   浏览次数:97
摘要:PA6 7335F|美国杜邦 PA6 7335F物性黄卡|PA6 7335F价格,DuPont Performance Polymers Zytel® 7335F NC010 Nylon 6 (Unverified Data**) Polymer,Thermoplastic,Nylon,Nylon 6 DuPont Performance Polymers

DuPont Performance Polymers Zytel® 7335F NC010 Nylon 6 (Unverified Data**)

Polymer,Thermoplastic,Nylon,Nylon 6

DuPont Performance Polymers

产品说明:

Zytel® 7335F NC010 is a nucleated, lubricated polyamide 6 resin for injection molding.

Information provided by DuPont Performance Polymers

DuPont Performance Polymers Zytel® 7335F NC010 Nylon 6 (Unverified Data**) 物性表(PA6 7335F最新价格

物理性能额定值 (公制)额定值 (英制)测试方法
密度1.13  g/cc0.0408  lb/in³DAM; ISO 1183
Water Absorption3.0 %

@Temperature 23.0 °C

3.0 %

@Temperature 73.4 °F

Equilibrium 50%RH; DAM; ISO 62, Similar to

9.0 %

@Temperature 23.0 °C

9.0 %

@Temperature 73.4 °F

Saturation, immersed; DAM; ISO 62, Similar to
线性成型收缩率0.0075  cm/cm

@Thickness 1.60 mm

0.0075  in/in

@Thickness 0.0630 in

DAM

0.010  cm/cm

@Thickness 3.20 mm

0.010  in/in

@Thickness 0.126 in

DAM
线性成型收缩率,Flow0.0060  cm/cm

@Thickness 2.00 mm

0.0060  in/in

@Thickness 0.0787 in

DAM; ISO 294-4
线性成型收缩率,横向0.0080  cm/cm

@Thickness 2.00 mm

0.0080  in/in

@Thickness 0.0787 in

DAM; ISO 294-4
机械性能额定值 (公制)额定值 (英制)测试方法
抗张强度(屈服)55.0  MPa

@Temperature 23.0 °C

7980  psi

@Temperature 73.4 °F

50%RH; ISO 527

90.0  MPa

@Temperature 23.0 °C

13100  psi

@Temperature 73.4 °F

DAM; ISO 527
伸长率 (断裂)9.0 %

@Temperature 23.0 °C

9.0 %

@Temperature 73.4 °F

DAM; nominal; ISO 527

15 %

@Temperature 23.0 °C

15 %

@Temperature 73.4 °F

50mm/min; DAM; ISO 527

>= 50 %

@Temperature 23.0 °C

>= 50 %

@Temperature 73.4 °F

50mm/min; 50%RH; ISO 527

>= 50 %

@Temperature 23.0 °C

>= 50 %

@Temperature 73.4 °F

50%RH; nominal; ISO 527
Elongation at Yield3.8 %

@Temperature 23.0 °C

3.8 %

@Temperature 73.4 °F

DAM; ISO 527

24 %

@Temperature 23.0 °C

24 %

@Temperature 73.4 °F

50%RH; ISO 527
拉伸模量1.40  GPa

@Temperature 23.0 °C

203  ksi

@Temperature 73.4 °F

50%RH; ISO 527

3.60  GPa

@Temperature 23.0 °C

522  ksi

@Temperature 73.4 °F

DAM; ISO 527
简支梁无缺口冲击强度6.00  J/cm²

@Temperature -30.0 °C

28.6  ft-lb/in²

@Temperature -22.0 °F

50%RH; ISO 179/1eU

7.00  J/cm²

@Temperature 23.0 °C

33.3  ft-lb/in²

@Temperature 73.4 °F

DAM; ISO 179/1eU

11.0  J/cm²

@Temperature -30.0 °C

52.3  ft-lb/in²

@Temperature -22.0 °F

DAM; ISO 179/1eU

12.0  J/cm²

@Temperature 23.0 °C

57.1  ft-lb/in²

@Temperature 73.4 °F

50%RH; ISO 179/1eU
简支梁缺口冲击强度0.250  J/cm²

@Temperature -30.0 °C

1.19  ft-lb/in²

@Temperature -22.0 °F

DAM; ISO 179/1eA

0.300  J/cm²

@Temperature -30.0 °C

1.43  ft-lb/in²

@Temperature -22.0 °F

50%RH; ISO 179/1eA

0.450  J/cm²

@Temperature 23.0 °C

2.14  ft-lb/in²

@Temperature 73.4 °F

DAM; ISO 179/1eA

1.80  J/cm²

@Temperature 23.0 °C

8.57  ft-lb/in²

@Temperature 73.4 °F

50%RH; ISO 179/1eA
电气性能额定值 (公制)额定值 (英制)测试方法
体积电阻率1.00e+11  ohm-cm

@Temperature 23.0 °C

1.00e+11  ohm-cm

@Temperature 73.4 °F

50%RH; ASTM D257

1.00e+11  ohm-cm

@Temperature 23.0 °C

1.00e+11  ohm-cm

@Temperature 73.4 °F

50%RH; IEC 60093

>=  1.00e+15  ohm-cm

@Temperature 23.0 °C

>=  1.00e+15  ohm-cm

@Temperature 73.4 °F

DAM; IEC 60093

1.00e+17  ohm-cm

@Temperature 23.0 °C

1.00e+17  ohm-cm

@Temperature 73.4 °F

DAM; ASTM D257

1.00e+17  ohm-cm

@Temperature 23.0 °C

1.00e+17  ohm-cm

@Temperature 73.4 °F

DAM; IEC 60093
Surface Resistance1.00e+11  ohm

@Temperature 23.0 °C

1.00e+11  ohm

@Temperature 73.4 °F

50%RH; ASTM D257

1.00e+11  ohm

@Temperature 23.0 °C

1.00e+11  ohm

@Temperature 73.4 °F

50%RH; IEC 60093

1.00e+13  ohm

@Temperature 23.0 °C

1.00e+13  ohm

@Temperature 73.4 °F

DAM; ASTM D257
介电常数3.3

@Frequency 1.00e+6 Hz, Temperature 23.0 °C

3.3

@Frequency 1.00e+6 Hz, Temperature 73.4 °F

DAM; ASTM D150

3.6

@Frequency 100 Hz, Temperature 23.0 °C

3.6

@Frequency 100 Hz, Temperature 73.4 °F

DAM; ASTM D150

3.6

@Frequency 1000 Hz, Temperature 23.0 °C

3.6

@Frequency 1000 Hz, Temperature 73.4 °F

DAM; ASTM D150

4.2

@Frequency 100 Hz, Temperature 23.0 °C

4.2

@Frequency 100 Hz, Temperature 73.4 °F

DAM; IEC 60250
介电强度13.5  kV/mm

@Thickness 3.20 mm, Temperature 23.0 °C

343  kV/in

@Thickness 0.126 in, Temperature 73.4 °F

50%RH; Short Time; ASTM D149

16.3  kV/mm

@Thickness 3.20 mm, Temperature 23.0 °C

414  kV/in

@Thickness 0.126 in, Temperature 73.4 °F

DAM; Short Time; ASTM D149
耗散因数0.010

@Frequency 1000 Hz, Temperature 23.0 °C

0.010

@Frequency 1000 Hz, Temperature 73.4 °F

DAM; ASTM D150

0.010

@Frequency 100 Hz, Temperature 23.0 °C

0.010

@Frequency 100 Hz, Temperature 73.4 °F

DAM; ASTM D150

0.020

@Frequency 1.00e+6 Hz, Temperature 23.0 °C

0.020

@Frequency 1.00e+6 Hz, Temperature 73.4 °F

DAM; ASTM D150

0.030

@Frequency 100 Hz, Temperature 23.0 °C

0.030

@Frequency 100 Hz, Temperature 73.4 °F

DAM; IEC 60250

0.11

@Frequency 1.00e+6 Hz, Temperature 23.0 °C

0.11

@Frequency 1.00e+6 Hz, Temperature 73.4 °F

50%RH; ASTM D150

0.23

@Frequency 1000 Hz, Temperature 23.0 °C

0.23

@Frequency 1000 Hz, Temperature 73.4 °F

50%RH; ASTM D150

0.37

@Frequency 100 Hz, Temperature 23.0 °C

0.37

@Frequency 100 Hz, Temperature 73.4 °F

50%RH; ASTM D150
相比耐漏电起痕指数(CTI)600  V

@Temperature 23.0 °C

600  V

@Temperature 73.4 °F

DAM; IEC 60112
热性能额定值 (公制)额定值 (英制)测试方法
线形热膨胀系数 - 流动500  µm/m-°C

@Temperature 23.0 - 55.0 °C

278  µin/in-°F

@Temperature 73.4 - 131 °F

DAM; ASTM E 831

500  µm/m-°C

@Temperature 23.0 - 55.0 °C

278  µin/in-°F

@Temperature 73.4 - 131 °F

DAM; ISO 11359-1/-2
线性热膨胀系数,横向流动92.0  µm/m-°C

@Temperature 23.0 - 55.0 °C

51.1  µin/in-°F

@Temperature 73.4 - 131 °F

DAM; ASTM E 831

92.0  µm/m-°C

@Temperature 23.0 - 55.0 °C

51.1  µin/in-°F

@Temperature 73.4 - 131 °F

DAM; ISO 11359-1/-2
熔融温度221  °C430  °F10°C/min; DAM; ISO 11357-1/-3
载荷下热变形温度(0.46 MPa)175  °C347  °FDAM; ISO 75-1/-2
载荷下热变形温度(1.8 MPa)65.0  °C149  °FDAM; ISO 75-1/-2
可燃性(UL94)HB

@Thickness 1.50 mm

HB

@Thickness 0.0591 in

DAM; UL94

HB

@Thickness 1.50 mm

HB

@Thickness 0.0591 in

DAM; IEC 60695-11-10
加工性能额定值 (公制)额定值 (英制)测试方法
加工(熔体)温度260 - 280  °C500 - 536  °FDAM

270  °C518  °FDAM; Optimum
模具温度70.0  °C158  °FDAM; optimum

50.0 - 90.0  °C122 - 194  °FDAM
干燥温度80.0  °C176  °FDAM
干燥时间2.00 - 4.00  hour2.00 - 4.00  hourDAM
水分含量<= 0.20 %<= 0.20 %DAM
材料描述
测试方法
添加剂LubricantDAM
外观Natural ColorDAM
Drying RecommendedYes, if moisture content of resin exceeds recommended levelDAM
特性Chemical Resistance, GoodDAM

Fatigue ResistantDAM

Fuel ResistantDAM

General PurposeDAM

Grease ResistantDAM

Mold Release, GoodDAM

NucleatedDAM

Oil ResistantDAM
形式PelletsDAM
GenericNylon 6DAM
Material StatusCurrentDAM
部件标识代码>PA6<ISO 11469; DAM
Polymer FamilyPolyamideDAM
Polymer TypePA6DAM
加工方法Injection MoldingDAM
产品分类Unreinforced ResinsDAM
树脂识别PA6ISO 1043; DAM
符合RoHS指令Contact ManufacturerDAM
Ultrasonic WeldableYesDAM
用途Appliance ComponentsDAM

Automotive ApplicationsDAM


热门关键词

PTFE  PVDF  PFA  FEP  PPA  PA6  PA66  PA46  PA612 

相关文章

联系我们

咨询热线:0512-53263079

微信号:tangxiangxiang199

邮箱:411476171@qq.com

地址: 上海市金山区张堰镇松金路275号

官方公众号

关注公众号获取更多有用资讯

用手机扫描二维码关闭
二维码